Method for coating metal surfaces of substrates and objects coated in accordance with said method

ABSTRACT

The invention relates to a method for coating surfaces, to a corresponding coating, and to the use of the objects coated in accordance with said method. The invention relates to a method for coating metal surfaces of substrates, comprising or consisting of the following steps: I. providing a substrate having a cleaned metal surface, II. contacting and coating metal surfaces with an aqueous composition in the form of a dispersion and/or suspension, IX. optionally rinsing the organic coating, and X. drying and/or baking the organic coating or XI. optionally drying the organic coating and coating with a coating composition of the same type or a further coating composition before a drying process and/or baking process, wherein in step II the coating is performed with an aqueous composition in the form of a dispersion and/or suspension containing 2.5 to 45 wt % of at least one non-ionic stabilized binder and 0.1 to 2.0 wt % of a gelling agent, wherein the aqueous composition has a pH value in the range of 0.5 to 7 and forms, with the cations eluted from the metal surface in the pretreatment step and/or during the contacting in step II, a coating based on an ionogenic gel.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. patent application Ser. No. 14/902,979, filed on Jan. 5, 2016, which is a national stage entry of PCT/EP2014/064857, filed on Jul. 10, 2014, which claims the benefit of priority to German Patent Application No. 102013213498.3, filed on Jul. 10, 2013, which are incorporated by reference in their entirety herein.

The invention relates to a method for coating surfaces, a corresponding coating and the use of the objects coated according to this method. There are numerous methods for producing homogeneous coatings on metallic surfaces in particular by means of immersion methods. In doing so, the following techniques are preferably used for creating anticorrosion coatings consisting primarily of an organic matrix and/or organic and/or inorganic additive components.

The traditional methods are based on use of the rheological properties of the formulations that are used in order to achieve a complete coating of a joined workpiece. Although an accumulation of coating material in critical locations can be reduced by continuous rotation of the respective workpiece after the immersion process, it is impossible with this method to achieve a completely homogeneous coating. In addition, defects such as bubbles and pits that have a negative effect on the quality of the coating as a whole may occur in locations with larger amounts of coating during the drying and/or crosslinking process.

Electrophoretic methods avoid these problems by using an electric current to deposit a uniform coating in immersion. With this method it is possible to homogeneous coatings on metallic workpieces. The coatings that are deposited exhibit extremely good adhesion in the wet state to the metallic substrate, which allows treatment of the workpiece in a subsequent rinsing step without separation of the coating. As a result, the aforementioned locations on the workpiece which are difficult to access can be freed of excess coating solution and therefore no defects can be formed during the drying process. This technique has the disadvantage that, in addition to the amount of electricity required and, in addition to suitable immersion basins, which result in increased costs and also so-called edge alignment, occur because electric fields are built up non-homogeneously on macroscopic edges, and the edges are coated uniformly and possibly even incompletely. In the design of the workpieces, it is also necessary to avoid cavities because an effect comparable to the Faraday cage phenomenon occurs in these locations. Because of the reduction in the electric field strengths required for deposition, only a greatly reduced coating can be applied by this method (wrap-around problem) or none at all in such regions of the workpiece, which results in a negative effect on the coating quality. In addition, this technique has the following disadvantages in electro dip coating (EDC) such as in cathodic dip coating (CDC): a corresponding immersion bath has a very complex structure, including all the electric and mechanical devices of temperature management, power supply and electrical installation, circulation devices and additional devices, including disposal of the anolyte acid formed in electrolytic coating and with ultrafiltration for recycling the coating as well as control devices. The process management also requires a very high technical complexity, due to the high amperages and large quantities of energy in both the standardization of the electric parameters based on the bath volume and the accurate adjustment of all process parameters and in maintenance and cleaning of the installation.

The known autophoretic processes are based on a currentless concept, consisting of a pickling attack on the substrate surface, in which metal ions are dissolved out of the surface and an emulsion is coagulated because of the concentration of metallic ions at the resulting interface. Although these methods do not exhibit the aforementioned restriction of the electrolytic methods with respect to the Faraday cage effect, the coatings formed in the process must be set in a complex multistage immersion process after the initial activation step. In addition, the pickling attack leads to unavoidable contamination of the active zone by metal ions that must be removed from the zones. Furthermore, the method is based on a chemical deposition process that is not self-regulating and cannot be terminated on demand, e.g., due to powering down the electric current in the electrolytic processes. Thus, the development of a layer that is too thick is unavoidable with a longer dwell time of the metallic substrates in the active zones.

There has long been a desire to form homogenous coatings in an immersion process efficiently and inexpensively in order to produce the most closed possible and essentially level coatings with a greater thickness from them.

The object is therefore a method for coating metallic surfaces of substrates, comprising or consisting of the steps:

-   I. Supplying a substrate having a cleaned metallic surface, -   II. Contacting and coating metallic surfaces with an aqueous     composition in the form of a dispersion and/or suspension, -   III. Optionally rinsing the organic coating and -   IV. Drying and/or baking the organic coating or -   V. Optionally drying the organic coating and forming another coating     having a similar or additional coating composition before drying     and/or baking,     wherein in step II, the coating is applied with an aqueous     composition in the form of a dispersion and/or suspension containing     2.5 to 45 wt % of at least one nonionically stabilized binder and     0.1 to 2.0 wt % of a gelling agent, wherein the aqueous composition     has a pH in the range of 0.5 to 7 and a coating based on an     ionogenic gel is formed, with cations dissolved out of the metallic     surface in the pretreatment step and/or during the contacting in     step II.

The nonionically stabilized binder used according to the invention is selected on the basis of the test described as shown below:

-   1) preparing an aqueous mixture of deionized water, 0.5 wt % of the     gelling agent and 10 wt % of the dispersion to be investigated; -   2) adjusting the mixture to a pH of 2 to 3 with the help of     hexafluorozirconic acid; -   3) immersing a cleaned substrate in the solution described above for     5 minutes at room temperature; -   4) in the case of deposition of a coating, a cross-check is carried     out (without the gelling agent); to do so, a mixture is prepared     from deionized water, 10 wt %, and the dispersion to be     investigated; -   5) the mixture prepared in step 4) is again adjusted to a starting     pH of 2-3 by means of hexafluorozirconic acid, and -   6) the test described in step 3) is repeated.

If an organic deposition is formed on the substrate according to step 3) and no deposition occurs in step 6) (without the gelling agent), then the nonionically stabilized binder is suitable for the method according to the invention.

The coating according to the invention has a single layer structure, wherein either a more or less homogenous coating is formed or a coating in which the (polymer) particles accumulate to a somewhat greater extent close to the metallic surface is formed and/or may occur.

According to the invention, the substrates with a metallic surface to be coated are understood as follows: metals, metal-coated surfaces or metal surfaces pretreated with primers, from which metal cations can still be released. In particular the term “surface(s) to be coated” in the sense of this patent application includes surfaces of metallic objects and/or metallic particles, which may optionally be precoated with a metallic coating based on zinc or a zinc alloy and/or with at least one coating of a pretreatment composition or treatment composition, for example, based on chromate, Cr³⁺, Ti compound, Zr compound, silane/silanol/siloxane/polysiloxane and/or organic polymer.

Of the metallic materials, fundamentally all types of metallic materials are possible, in particular those made of aluminum, iron, copper, titanium, zinc, tin and/or alloys containing aluminum, iron, steel, copper, magnesium, nickel, titanium, zinc and/or tin, wherein they may also be used side by side and/or one after the other. The material surfaces may optionally also be precoated, for example, with zinc or an alloy containing aluminum and/or zinc.

Fundamentally all types of objects made of a metallic material or provided with at least one metallic coating may be used as the object to be coated. Especially preferred objects include in particular strips (coils), sheet metal, parts such as small parts, joined components, components with complex shapes, profiles, rods and/or wires.

The term “currentless coating” in the sense of this patent application means that in contrast with the known electrolytic methods for producing the follow-up coating, an electric voltage of less than 100 V is applied externally in coating with the composition containing the solution and/or dispersion (=suspension and/or emulsion) in contrast with the known electrolytic methods for producing the follow-up coating.

The invention preferably relates to a method in which the gelling agent a) contains or consists of at least one polysaccharide, based on glycogens, amyloses, amylopectins, calloses, agar, algins, alginates, pectins, carrageenan, celluloses, chitins, chitosans, curdlans, dextrans, fructans, collagens, gellan gum, gum arabic, starch, xanthans, gum tragacanth, karayans, tara gum and glucomannans; b) at least one gelling agent of natural origin, based on polyamino acids, collagens, polypeptides, lignins and/or c) at least one synthetic gelling agent, based on polyamino acids, polyacrylic acids, polyacrylic acid copolymers, acrylamide copolymers, lignins, polyvinyl sulfonic acid, polycarboxylic acids, polyphosphoric acids or polystyrenes.

The gelling agent especially preferably contains or consists of at least one polysaccharide based on pectins and/or gellan gum.

The method according to the invention is preferably one in which the aqueous composition and/or the organic coating produced from it contains at least one type of cations selected from those based on salts with a cationic effect, selected from the group consisting of melamine salts, nitroso salts, oxonium salts, ammonium salts, salts with quaternary nitrogen cations, salts of ammonium derivatives and metal salts of Al, B, Ba, Ca, Cr, Co, Cu, Fe, Hf, In, K, Li, Mg, Mn, Mo, Na, Nb, Ni, Pb, Sn, Ta, Ti, V, W, Zn and/or Zr.

The term “copolymers” in the sense of this patent application describes polymers made up of two or more different types of monomer units. Copolymers here can be divided into five classes, as will be illustrated on the basis of a binary copolymer made up of two different comonomers A and B:

-   1. Random copolymers in which the distribution of the two monomers     in the chain is random (AABABBBABAABBBABBABAB . . . ); -   2. Gradient copolymers, resembling random copolymers in principle,     but having a variable amount of monomer in the course of the chain     (AAAAAABAABBAABABBBAABBBBBB); -   3. Alternating copolymers with a regular arrangement of the monomers     along the chain (ABABABABABABABABABAB . . . ); -   4. Block copolymers consisting of longer sequences or blocks of each     monomer (AAAAAAAAABBBBBBBBBBBB . . . ), wherein depending on the     number of blocks, we can also speak of diblock, triblock,     multi-block copolymers; -   5. Graft copolymers, in which blocks of a monomer are grafted onto     the backbone of another monomer.

The term “derivatives” in the sense of this patent application denotes a derived substance having a structure similar to that of a corresponding basic substance. Derivatives are substances, whose molecules have another atom or a different atomic group instead of an H atom or a functional group and/or in which one or more atoms/atomic groups have been removed.

The term “polymer(s)” in the sense of this patent application denotes monomer(s), oligomer(s), polymer(s), copolymer(s), block copolymer(s), graft copolymer(s), mixtures thereof and their compounds on an organic and/or essentially organic basis. The “polymer(s)” in the sense of this patent application is (are) usually present primarily or entirely as polymer(s) and/or copolymer(s).

The method according to the invention is especially preferably one in which the aqueous composition and/or the organic coating produced from it contain(s) an amount of film-forming binders based on polyacrylates, polyurethanes, polyepoxides and/or their hybrids.

So-called polyacrylate-polyurethane hybrid resins of this type can be differentiated according to hybrid systems which are created by simply mixing the different dispersions (blends or formulations) into those having a chemical bond between the different types of polymers and those in which the different classes of polymers form interpenetrating networks (IPN).

Such polyurethane-polyacrylate hybrid dispersions are usually prepared by emulsion polymerization of a vinyl polymer (“polyacrylate”) in an aqueous polyurethane dispersion. However, it is also possible to produce the polyurethane-polyacrylate hybrid dispersion as a secondary dispersion.

Aqueous polyacrylate-polyepoxy hybrid dispersions are usually prepared by addition reactions of a bifunctional epoxy with bifunctional amine monomer building blocks and then a reaction with a polyacrylate having enough carboxyl functions. As with polyurethane secondary dispersions, water dispersibility can be achieved by carboxylate groups, for example, which have been converted into anionic groups with amines and then dispersing in water.

Hybrid dispersions for forming a layer on the substrate may preferably also contain, in addition to polyurethane and polyepoxy ingredients, organic polymers and/or copolymers based on polyvinyl alcohols, polyvinyl acetates, polybutyl acrylates and/or other acrylic acid esters. Acrylic acid esters are esters derived from acrylic acid (CH₂═CH—COOH) and thus having the functional group (CH₂═CH—COOR). Acrylic acid methyl esters, acrylic acid ethyl esters, acrylic acid butyl esters and ethyl hexyl acrylate are produced in large quantities. The main use of acrylic acid esters is in homo- and copolymers which contain, for example, acrylic acid, acrylamides, methacrylates, acrylonitrile, fumaric acids, itaconic acid, maleates, vinyl acetate, vinyl chloride, styrene, butadiene and unsaturated polyesters, polyepoxide esters, polyacrylamides, polyacrylic acids, polycarbonates, polyesters, polyethers, polystyrene butadienes, poly(meth)acrylic acid esters, polyvinyl acetate copolymers with acrylic acid esters and/or copolymers with dibutyl maleate and/or with vinyl esters of at least one Koch acid, polyethylenes, polyvinyl chlorides, polyacrylonitriles, polyepoxies, polyurethanes, polyacrylates, polymethacrylates, polyesters, polyamides, polytetrafluoroethylenes, polyisobutadienes, polyisoprenes, silicones, silicone rubbers and/or their derivatives. These are present in particular in amounts of at least 50 wt % of the solid ingredients and active ingredients in the aqueous composition.

The term “pretreatment” refers to a treatment (=bringing the surfaces to be coated in contact with a composition, usually liquid), in which another coating is applied to protect the layer sequence and the object such as at least one lacquer, for example, optionally after a subsequent coating.

In the case of a prior pretreatment before activation of a surface with an activating agent that should help to electrostatically charge the surface, the surfaces to be treated may first be given an alkaline cleaning, if necessary, and optionally brought in contact with a composition for pretreatment, the latter in particular to form a conversion layer. Then the surfaces treated and/or coated in this way may optionally be coated and/or optionally oiled with a primer and/or with an optionally reshapeable protective layer, in particular with an anticorrosion primer. Oiling serves in particular to provide temporary protection for the treated and/or coated surfaces, in particular metallic surfaces.

As a pretreatment, fundamentally any type of pretreatment is possible. For example, aqueous pretreatment compositions based on phosphate, phosphonate, silane/silanol/siloxane/polysiloxane, lanthanide compound, titanium compound, hafnium compound, zirconium compound acid, metal salt and/or organic polymer may be used.

In further treatment of these coated substrates, an alkaline cleaning in particular may be performed, if needed, regardless of whether or not oil has been applied previously.

A coating with an anticorrosion primer such as, for example, a welding primer can provide additional corrosion protection in particular in cavities and in difficult to access sections of a substrate, while facilitating shapeability and/or joinability, for example, in folding, gluing and/or welding. In industrial practice, an anticorrosion primer could be used in particular when the substrate, such as sheet metal, coated with it is to be shaped after coating with the anticorrosion primer and/or is to be joined to another component and if additional coatings are only then to be applied. If an anticorrosion primer is additionally applied beneath the activation layer and beneath the polymer coating in this set of operations, then improved corrosion prevention is usually achieved.

The term “essentially rinse-fast” in the sense of this patent application means that under the conditions of the respective installation and process sequence, the last coating, respectively, is not removed entirely by a rinsing operation (=rinsing), so that a coating, preferably a closed coating, can be produced.

In the method according to the invention, a wide variety of types of particles, particle sizes and particle shapes may be used as the particles.

The particles to be used in the aqueous composition for forming the layer may preferably be oxides, hydroxides, carbonates, phosphates, phosphosilicates, silicates, sulfates, organic polymers including copolymers and their derivatives, waxes and/or compounded particles, in particular those based anticorrosion pigments, organic polymers, waxes and/or compounded particles and/or mixtures thereof. They preferably have particle sizes in the range of 5 nm to 15 μm, from 8 nm to 5 μm or from 15 nm to 1.5 μm, in particular from 30 nm to 700 nm or from 50 nm to 500 nm. They are preferably water-insoluble particles.

Compounded particles have a mixture of at least two different substances in one particle. Compounded particles may often have other substances with very different properties. They may, for example, contain the composition for a lacquer entirely or partially, optionally even containing substances not in particulate form, such as surfactants, defoaming agents, dispersants, lacquer aids, additional types of additives, dyes, corrosion inhibitors, weakly water-soluble anticorrosion pigments and/or other substances that are customary and/or known for the corresponding mixtures. Such lacquer ingredients may be suitable and/or may often be used for organic coatings for shaping, for anticorrosion primers and other primers, for colored lacquers, fillers and/or clear lacquers.

An anticorrosion primer usually contains electrically conductive particles and can be welded electrically. In generally it is often preferably here that a) a mixture of chemically and/or physically different particles, b) particles, aggregates and/or agglomerates of chemically and/or physically different particles and/or c) compounded particles are used in the composition and/or in the particle layer formed from the composition.

In many cases, it is preferable for the composition containing the particles and/or the particle layer formed from it to also contain in addition to at least one type of particles, at least one non-particulate substance, in particular additives, dyes, corrosion inhibitors and/or weakly water-soluble anticorrosion pigments. In particular colored particles and/or optionally a limited amount of electrically conductive particles, in particular based on fullerenes and other carbon compounds with graphite-like structures and/or carbon black, optionally also nano containers and/or nanotubes may also be present as particles in the composition and/or in the particle layer formed from it. On the other hand, coated particles, chemically and/or physically modified particles, core-shell particles, compounded particles from various substances, encapsulated particles and/or nano containers may be used in particular as particles in the composition and/or in the coating formed from it.

With the method according to the invention, it is preferable for the composition containing the particles, the particle layer formed from it and/or the coating formed from it by creating a film and/or crosslinking the composition to contain, in addition to at least one type of particles, also at least one dye, one colored pigment, one anticorrosion pigment, one corrosion inhibitor, one conductivity pigment, another type of particles, a silane/silanol/siloxane/polysiloxane/silazane/polysilazane, a lacquer additive and/or an additive such as, for example, at least one surfactant, one defoaming agent and/or one dispersant.

With the method according to the invention, it is preferable for the composition and/or the coating formed from it to contain, either partially or completely, in addition to at least one type of particles and optionally in addition to at least one non-particulate substance, a chemical composition for a primer, a lacquer such as, for example, a filler, a top coat and/or a clear coat.

In many embodiments, pigments and/or additives, such as those often used in lacquers and/or primers, are recommended as additives to the organic polymers of the particles.

Formation of a film can be improved by use of thermoplastic polymers and/or by adding substances that serve as temporarily plasticizers. Film-forming aids act as specific solvents, which soften the surface of the polymer particles and thus enable their fusion. It is advantageous here if these plasticizers remain in the aqueous composition for a sufficiently long period of time, on the one hand, to be able to act on the polymer particles for a long time and then evaporate and thus escape from the film. Furthermore it is advantageous if a residual water content is also present for a sufficiently long period of time during the drying process.

So-called long alcohols, in particular those having 4 to 20 carbon atoms, are advantageous as film-forming aids:

-   such as butanediol, -   butyl glycol, -   butyl diglycol, -   ethylene glycol ether, such as ethylene glycol monobutyl ether, -   ethylene glycol monoethyl ether, -   ethylene glycol monomethyl ether, -   ethyl glycol propyl ether, -   ethylene glycol hexyl ether, -   diethylene glycol methyl ether, -   diethylene glycol ethyl ether, -   diethylene glycol butyl ether, -   diethylene glycol hexyl ether or a -   polypropylene glycol ether such as -   propylene glycol monomethyl ether, -   dipropylene glycol monomethyl ether, -   tripropylene glycol monomethyl ether, -   propylene glycol monobutyl ether, -   dipropylene glycol monobutyl ether, -   tripropylene glycol monobutyl ether, -   propylene glycol monopropyl ether, -   dipropylene glycol monopropyl ether, -   tripropylene glycol monopropyl ether, -   propylene glycol phenyl ether, -   trimethyl pentane diol diisobutyrate, -   a polytetrahydrofuran, -   a polyether polyol and/or a polyester polyol.

Crosslinking may take place, for example, with certain reactive groups, such as isocyanate groups, isocyanurate groups, phenol groups and/or melamine groups.

The subsequent coating is preferably dried in such a manner that, in particular, any organic polymer particles that are present can form a film so that a larger or completely homogenous coating is formed. In many embodiments, the drying temperatures can be selected to be so high that the organic polymer ingredients are able to crosslink.

In the method according to the invention, it is preferable in some embodiments that a particle layer containing essentially organic particles is formed and is crosslinked and/or a film is formed in drying, for example. The formation of a film in many embodiments takes place even without the presence of film-forming aids. The particles of the coating here preferably form a closed coating or an essentially closed coating in particular when the particles are present primarily or entirely as organic polymers, in particular in drying. It is often preferable for the drying temperature of a coating consisting primarily or entirely of organic polymers to be selected, so that a closed or essentially closed coating is formed. If necessary, at least one film-forming may be added to form the film, in particular a film-forming aid, based on at least one long-chain alcohol. In embodiments having a plurality of particle layers one above the other, all the particle layers are preferably applied first and then crosslinked and/or the film is formed from them together.

The amount of at least one film-forming aid in the aqueous composition—in particular in the bath—may preferably be 0.01 to 50 g/L, based on the solids including the active ingredients, especially preferably 0.08 to 35 g/L, most especially preferably 0.2 to 25 g/L or 0.5 to 16 g/L, in particular 1 to 12 g/L or 4 to 6 g/L. The weight ratio of the amounts of organic film-forming agent to the amounts of film-forming aids in the aqueous composition—in particular in the bath—may vary in a wide range and in particular may be ≤(100:0.1). This ratio is preferably in the range of 100:10 to 100:0.2 or from 100:2.5 to 100:0.6, especially preferably in the range of 100:2 to 100:0.75 or from 100:1.4 to 100:1.

It is often preferable here for the drying, film forming and/or crosslinking to take place in the temperature range of 50 to 260° C., especially preferably in the temperature range from 120 to 220° C., based on the oven temperature and/or based on the peak metal temperature (PMT). The selected temperature range depends largely on the type and amount of organic ingredients and optionally also the inorganic ingredients and optionally also their film-forming temperatures and/or crosslinking temperatures.

The invention preferably relates to a method in which the aqueous composition and/or the organic coating produced from it contains an amount of at least one complexing agent for metal cations or a polymer which is modified for complexing metal cations.

The method according to the invention is preferably one in which the aqueous composition and/or the organic coating produced from it contains at least one complexing agent selected from those based on maleic acid, alendronic acid, itaconic acid, citraconic acid or mesaconic acid or the anhydrides or hemiesters of these carboxylic acids.

The aqueous composition and/or the organic coating produced from it advantageously contain(s) at least one emulsifier.

It is especially preferable that the aqueous composition and/or the organic coating produced from it contains at least one emulsifier selected from those based on anionic emulsifiers.

The aqueous composition and/or the organic coating produced from it preferably contain(s) a mixture of at least two different anionic polyelectrolytes.

The aqueous composition and/or the organic coating produced from it especially preferably contain(s) a mixture of two pectins.

The aqueous composition and/or the organic coating produced from it also preferably contains as the gelling agent at least one anionic polysaccharide selected from those with a degree of esterification and/or a degree of amidation of the carboxy function in the range of 1 to 75% based on the total number of alcohols and carboxy groups.

The aqueous composition and/or the organic coating produced from it most especially preferably contains as the gelling agent at least one anionic polysaccharide and/or at least one anionic polyelectrolyte selected from those having a molecular weight in the range of 500 to 1,000,000 g/mol⁻¹.

In the method according to the invention, it is especially preferable that the anionic polyelectrolytes are or have been modified with adhesion-promoting adhesive groups selected from the group consisting of chemical groups of multifunctional epoxies, isocyanates, primary amines, secondary amines, tertiary amines, quaternary amines, amides, imides, imidazoles, formamides, Michael reaction products, carbodiimides, carbenes, cyclic carbenes, cyclocarbonates, multifunctional carboxylic acids, amino acids, nucleic acids, methacrylamides, polyacrylic acids, polyacrylic acid derivatives, polyvinyl alcohols, polyphenols, polyols having at least one alkyl and/or aryl radical, caprolactam, phosphoric acids, phosphoric acid esters, epoxy esters, sulfonic acids, sulfonic acid esters, vinyl sulfonic acids, vinyl phosphonic acids, catechol, silanes as well as the silanols and/or siloxanes produced from them, triazines, thiazoles, thiazines, dithiazines, acetals, hemiacetals, quinones, saturated fatty acids, unsaturated fatty acids, alkyds, esters, polyesters, ethers, glycols, cyclic ethers, crown ethers, anhydrides as well as acetylacetones and β-diketo groups, carbonyl groups and hydroxyl groups.

Al, Cu, Fe, Mg and/or Zn is/are advantageously selected as the cations that are/have been dissolved out of the metallic surface and/or that are/have been added to the aqueous composition.

The aqueous composition preferably also contains a crosslinking agent selected from the group consisting of silanes, siloxanes, phenolic resin types or amines in an amount of 0.01 g/L to 50 g/L.

The aqueous composition especially preferably contains a crosslinking agent selected from the group consisting of silanes, siloxanes, phenolic resin types or amines in an amount of 0.01 g/L to 50 g/L.

In another embodiment of the invention, the aqueous composition contains complex titanium and/or zirconium fluorides in an amount of 0.001 g/L to 500 g/L.

The aqueous composition especially preferably contains complex titanium and/or zirconium fluorides in an amount of 0.01 g/L to 75 g/L.

The aqueous composition and/or the organic coating produced from it most especially preferably also contain(s) at least one additive selected from additives consisting of the group of foam suppressants, biocides, dispersion aids, film-forming aids, acidic and/or basic additives for adjusting the pH and thickeners and flow control agents.

Before bringing the metallic surfaces in contact with an aqueous composition and coating the metallic surfaces with the aqueous composition in process step II, the metallic surfaces are most especially preferably cleaned, pickled and/or pretreated.

The aqueous composition advantageously forms a coating based on ionogenic gel in which the dry film which is formed then or later has a thickness of at least 1 μm.

The organic coating especially preferably is formed in 0.05 to 20 minutes in an immersion bath and has a dry film thickness in the range of 5 to 100 μm after drying.

The invention also relates to an aqueous composition containing 2.5 to 45 wt % of at least one nonionically stabilized binder and 0.1 to 2.0 wt % of a gelling agent wherein the aqueous composition has a pH in the range of 0.5 to 7.

The aqueous composition is preferably a composition that contains in the dispersion of film-forming polymers an amount of organic particles based on polyacrylates, polyurethanes, polyepoxides and/or their hybrids, an amount of at least one complexing agent selected from those based on maleic acid, alendronic acid, itaconic acid, citraconic acid or mesaconic acid or anhydrides or hemiesters of these carboxylic acids and at least one anionic polyelectrolyte based on pectins or gellan gum.

It has been found that closed or essentially closed coatings having a layer thickness in the range of 1 μm to 250 μm, in particular in the range of 3 μm to 100 μm or 5 μm to 50 μm, can then be prepared from the surfaces coated according to the invention. The individual coatings may have corresponding layer thicknesses before and/or after their film-forming step and/or before their crosslinking.

It has been found that the surfaces coated according to the invention from which closed or essentially closed coatings are subsequently formed can be produced by much simpler and much less expensive methods than, for example, electro dip coatings, autophoretic dip coatings or powder coatings.

Furthermore, it has been found that such coatings produced according to the invention may be equivalent in their properties to the electro dip coatings, autophoretic dip coatings or powder coatings of industrial practice today if formulations prepared chemically accordingly in particular are used.

It has surprisingly been found that the method according to the invention, which is not or essentially not an electrolytic method, even in the event that it is supported to a minor extent by electric voltage, and therefore it is not usually necessary for an external electric voltage to be applied, can be operated easily without complex controls. This method can be used in a broad temperature range and even at room temperature, if the subsequent drying is omitted.

It has surprisingly been found that in the case of the method according to the invention, no complex control measures are required with respect to the application of the activating means in order to achieve a uniform and homogeneous coating and that high quality protective follow-up coatings are formed with a low consumption of chemicals, these coatings achieving thickness in the range of 500 nm to 30 μm.

It has surprisingly been found that the method according to the invention is a self-regulating method with regard to the deposition of the follow-up coating in particular and that no complex control measures are necessary in this method and high quality protective coatings are formed with a low consumption of chemicals.

It has surprisingly been found that the follow-up coatings deposited according to the invention form a homogenous layer with a uniform dry layer thickness even on a workpiece having a complex shape, and that these coatings are comparable in quality to a traditional paint layer applied by traditional electrophoretic or autophoretic deposition methods.

The coating according to the invention can preferably be used for coated substrates as wire, wire mesh, strip, sheet metal, profile, lining, parts for a vehicle or a flying object, elements for a household appliance, elements in construction, frameworks, guide rails, heating elements or fence elements, molded parts of a complex geometry or small parts such as screws, nuts, flanges or springs. It is especially preferably used in automotive engineering, construction, for appliance building, for household appliances or in the heating sector. Use of the method according to the invention is especially preferred for coating substrates, which have posed problems in coating with an electro dip coating.

The invention will now be explained in greater detail below on the basis of 16 exemplary embodiments and two comparative examples, using as substrates in step I:

-   I. 1: Electrolytically galvanized steel plate with a zinc layer     thickness of 5 μm, sheet metal thickness 081 mm;     -   2: Cold rolled steel, sheet metal thickness approximately 0.8         mm;     -   3: Aluminum alloy of grade AC 170, sheet metal thickness         approximately 1.0 mm and the following general treatment step         are carried out; -   II. Alkaline cleaning     -   30 g/L Gardoclean® S 5176 and 4 g/L Gardobond® Additive H 7406         from Chemetall GmbH prepared in drinking water according to         DIN 2000. The sheet metal plates were cleaned for 180 s by         spraying at 60° C. and then rinsed for 120 s within drinking         water and 120 s with deionized water by immersion. -   III. 1. Pretreatment based on zinc phosphate (Gardobond 26S of the     company Chemetall GmbH)     -   2. Pretreatment based on silane (Oxsilan 9810/2 from the company         Chemetall GmbH)

All the mixtures were applied to the respective substrate within 5 minutes by dipping at room temperature.

The pH values of the entire formulation were adjusted by means of aqueous solutions of phosphoric acid (10%) and ammonia (10%).

Binders

1: Dispersion A

Nonionically stabilized dispersion with a solids content of 50-54%, a pH of 5.0-6.0, a viscosity of 1500-3000 mPas and a density of 1.079 g/cm³. The data in the table is based on the amount of solution per liter of formulation and the resulting solids content is based on the formulation.

2: Dispersion B

Nonionically stabilized dispersion with a solids content of 50-54%, a pH of 5.0-6.0, a viscosity of 300-1500 mPas and a density of 1.079 g/cm³. The data in the table is based on the amount of solution per liter of formulation and the resulting solids content is based on the formulation.

3: Dispersion C

Anionically stabilized polyacrylate dispersion with a solids content of 40%, a pH of 3.0-5.0, a viscosity of 500-3000 mPas, a density of 1.04 g/cm³, particle size of approximately 160 mm and an OH number of approximately 25 mg KOH/g (solid resin). The data in the table is based on the amount of solution per liter of formulation and the resulting solids content is based on formulation.

Gelling Agent

A 1:1 mixture of polysaccharide with a molecular weight of approximately 70,000 g/mol, a degree of amidation of 11%, a degree of esterification of 41%, a degree of epoxidation of 0%, a galacturonic acid content of 88% and a polysaccharide with a molecular weight of approximately 70,000 g/mol, a degree of amidation of 0%, a degree of esterification of 38%, a degree of epoxidation of 0%, a galacturonic acid content of 85% are used as the gelling agent. To prepare the formulation, a 2% aqueous solution of the polysaccharide was used. The data in the table is based on the amount of solution per liter of formulation.

Additives

-   1: Hexafluorotitanic acid as an aqueous solution (20%) was used. The     data in the table is based on the amount of solution per liter of     formulation. -   2: Hexafluorozirconic acid was used as an aqueous solution (20%).     The data in the table is based on the amount of solution per liter     of formulation. -   3: 3-(Triethoxysilyl)propylamine (AMEO) was used. The data in the     table is based on the amount of solution per liter of formulation.     Pigments -   1: Gas black RCC pigment concentrate based on a dispersion resin for     applications in aqueous coating systems with pH values in the acidic     range, with a pigment content of 30%, a solids content of 38% and a     density of 1.17 g/cm³. -   2: Inorganically coated white pigment based on a titanium dioxide     rutile with a titanium dioxide content of 92%. -   3: Micronized white pigment based on a titanium dioxide rutile, with     organic and inorganic coatings.     Defoaming Agent -   1: Defoaming agent based on natural oils, emulsifiers and containing     1 wt % of the as-delivered form in water. The data in the table is     based on the amount of solution per liter of formulation. -   IV: Rinsing the organic coating:

The rinse after the organic coating serves to remove non-adhering constituents of the formulation and agglomerates of the formulation and to make the process sequence as close to reality as possible in the automobile industry because the rinsing with water is usually performed either as a dip rinse or as a spray rinse in the automobile industry.

-   V: Drying and/or crosslinking the coating

Drying or drying with film formed of the organic polymer ingredient in particular:

-   -   175° C. for 15 minutes

Parallel studies using an eddy current measurement device and scanning electron microscopy (SEM) have illustrated the fact that coatings according to the invention are produced, and then closed or mostly closed coatings can be formed from them by bringing the surfaces in contact with dispersions and/or formulations.

EXAMPLE 1

Substrate 1 was coated with a mixture consisting of 10 wt %, based on the total amount of the resulting mixture of dispersion A, and 0.5 wt % of the gelling agent, based on the total amount of the resulting mixture. If necessary, the mixture was adjusted to a pH of 2 with acid, preferably nitric acid and/or phosphoric acid, before being used. A dry film thickness of 20-30 μm was determined, based on measurements with an eddy current measurement instrument and SEM.

EXAMPLE 2

Experiment 1 was repeated with substrate 2 and a dry film thickness of 10-20 μm was determined by SEM.

EXAMPLE 3

Substrate 1 was coated with a mixture consisting of 10 wt %, based on the total amount of the resulting mixture of dispersion A and 0.5 wt % of the gelling agent, based on the total amount of the resulting mixture. The mixture was adjusted to a pH of 4 before use with acid, preferably nitric acid and/or phosphoric acid. Substrate 1 was pretreated according to III.1 by phosphating. A dry film thickness of 7-10 μm was determined based on a measurement with an eddy current measurement device and SEM.

EXAMPLE 4

Experiment 3 was repeated with substrate 2 and a dry film thickness of 7-10 μm was also determined with SEM.

EXAMPLE 5

Substrate 1 was coated with a mixture consisting of 10 wt %, based on the total amount of the resulting mixture, of dispersion A, and 0.5 wt % of the gelling agent, based on the total amount of the resulting mixture. If necessary, the mixture was adjusted to a pH of 4 with acid, preferably nitric acid and/or phosphoric acid, before use. Substrate 1 was pretreated with a silane according to III.2. A dry film thickness of 7-10 μm was determined, based on measurements with an eddy current measurement device and SEM.

EXAMPLE 6

Experiment 5 was repeated with substrate 2, and a dry film thickness of 7-10 μm was also determined using SEM.

EXAMPLE 7

Substrate 1 was coated with a mixture consisting of 5 wt % based on the total amount of the resulting mixture, of dispersion A and 0.5 wt % of the gelling agent, based on the total amount of the resulting mixture. Before use, the mixture was adjusted to a pH of 2 with acid, if necessary, preferably nitric acid and/or phosphoric acid. A dry film thickness of 10-15 μm was determined, based on measurement with an eddy current measurement device and SEM.

EXAMPLE 8

Experiment 7 was repeated with substrate 2, and a dry film thickness of 8-12 μm was also determined with SEM.

EXAMPLE 9

Substrate 1 was coated with a mixture consisting of 10 wt %, based on the total amount of the resulting mixture, of dispersion B and 0.5 wt % of the gelling agent, based on the total amount of the resulting mixture. Before use, the mixture was adjusted to a pH of 4 with acid, preferably nitric acid and/or phosphoric acid, if necessary. A dry film thickness of 5-8 μm was determined, based on measurements with an eddy current measurement device and SEM.

EXAMPLE 10

Experiment 9 was repeated with substrate 2 and a dry film thickness of 8-12 μm was also determined with SEM.

EXAMPLE 11

Substrate 1 was coated with a mixture consisting of 10 wt %, based on the total amount of the resulting mixture, of dispersion A and 0.5 wt % of the gelling agent, based on the total amount of the resulting mixture. Before use, the mixture was adjusted to a pH of 2 with acid, preferably nitric acid and/or phosphoric acid, if necessary. As an additive, 0.4 g/L hexafluorotitanic acid was added. A dry film thickness of 35-40 μm was determined, based on measurement with an eddy current measurement device and SEM.

EXAMPLE 12

Experiment 11 was repeated with substrate 2, and a dry film thickness of 20-25 μm was also determined with SEM.

EXAMPLE 13

Experiment 11 was repeated with substrate 3, and a dry film thickness of 3-5 μm was also determined using SEM.

EXAMPLES 14-15

As in Examples 11 to 13, substrates 1 to 3 were coated, except that 0.4 g/L hexafluorozirconic acid was added instead of 0.4 g/L hexafluorotitanic acid. A dry film thickness of 8-10 μm was determined for substrates 1 and 2 and 3-5 μm for substrate 3, based on measurements with an eddy current measurement device and SEM.

EXAMPLES 16-19

As in Examples 11 to 13, substrates 1 to 3 were coated except that, in addition to 0.4 g/L hexafluorotitanic acid, 3 g/L AMEO was also used as an additive. A dry film thickness of 30-35 μm was determined for substrate 1, 15-20 μm for substrate 2 and 3-5 μm for substrate 3, based on measurements with an eddy current measurement device and SEM.

EXAMPLES 20-23

As in Examples 11 to 13, substrates 1 to 3 were coated except that in addition to 0.4 g/L hexafluorotitanic acid, 3 g/L AMEO was also used as an additive. A dry film thickness of 8-10 μm was determined for substrates 1 and 2 and 3-5 μm for substrate 3, based on measurements with an eddy current measurement device and SEM.

EXAMPLES 24-26

As in Examples 11 to 13, substrates 1 to 3 were coated except that 3 g/L AMEO, 3 g/L gas black pigment and 5 g/L defoaming agent were added as an additive in addition to 0.4 g/L hexafluorotitanic acid. A dry film thickness of 30-35 μm was determined for substrate 1, 15-20 μm for substrate 2 and 3-5 μm for substrate 3, based on measurements with an eddy current measurement device and SEM.

The micrographs consistently show a homogenous layer has formed, which indicates a reliable, self-regulating and readily controllable coating method. 

The invention claimed is:
 1. An aqueous composition containing 2.5 to 45 wt % of at least one nonionically stabilized binder and 0.1 to 2.0 wt % of a gelling agent, wherein the aqueous composition has a pH in the range of 0.5 to 7, wherein the gelling agent contains at least one anionic polysaccharide, wherein the gelling agent further contains at least one anionic polyelectrolyte selected from the group consisting of anionic polyelectrolytes having a molecular weight in the range of 500 to 1,000,000 g/mol, and wherein the aqueous composition is in a form of a dispersion, a suspension, or a combination thereof.
 2. The aqueous composition according to claim 1 further containing one or more representatives selected from the group consisting of: a) a crosslinking agent selected from the group consisting of silanes, siloxanes, phenolic resins and amines in an amount of 0.01 g/L to 50 g/L, b) complex titanium, zirconium fluorides or a combination thereof in an amount of 0.01 g/L to 500 g/L, and c) at least one additive selected from the group consisting of defoaming agents, pigments, biocides, dispersion aids, film-forming aids, acidic additives for adjusting the pH, basic additives for adjusting the pH, thickeners and flow control agents.
 3. The aqueous composition according to claim 1, wherein the aqueous composition is configured to contact and coat a metallic surface in the form of at least one of a dispersion and suspension.
 4. The aqueous composition according to claim 3, wherein a coating is formed and is based on an ionogenic gel.
 5. The aqueous composition according to claim 4, wherein the coating comprises at least one of oxides, hydroxides, carbonates, phosphates, phosphosilicates, silicates, sulfates, organic polymers including copolymers and derivatives thereof, waxes, compounded particles, and mixtures thereof.
 6. The aqueous composition according to claim 1, wherein the aqueous composition further comprises film-forming binders selected from the group consisting of polyacrylates, polyurethanes, polyepoxides, and hybrids thereof.
 7. The aqueous composition according to claim 1, wherein the aqueous composition further comprises film-forming binders selected from the group consisting of organic polymers, copolymers based on polyvinyl alcohols, polyvinyl acetates, polybutyl acrylates, and other acrylic acid esters and are present in amounts of at least 50 wt % in the aqueous composition.
 8. The aqueous composition according to claim 7, wherein the aqueous composition further comprises film forming aids, and wherein a weight ratio of the film-forming binders to the film-forming aids is in the range of from 100:1.4 to 100:1.
 9. The aqueous composition according to claim 1, wherein the aqueous composition contains at least one type of cations selected from the group consisting of cations based on salts with a cationic effect selected from the group consisting of melamine salts, nitroso salts, oxonium salts, ammonium salts, salts with quaternary nitrogen cations, salts of ammonium derivatives, and metal salts of Al, B, Ba, Ca, Cr, Co, Cu, Fe, Hf, In, K, Li, Mg, Mn, Mo, Na, Nb, Ni, Pb, Sn, Ta, Ti, V, W, Zn, and Zr.
 10. The aqueous composition according to claim 1, wherein the aqueous composition contains at least one of a complexing agent for metal cations and a polymer that is modified for complexing metal cations.
 11. The aqueous composition according to claim 10, wherein the complexing agent is selected from the group consisting of maleic acid, alendronic acid, itaconic acid, citraconic acid, mesaconic acid, and anhydrides and hemiesters thereof.
 12. The aqueous composition according to claim 1, wherein the aqueous composition contains at least one emulsifier selected from the group consisting of anionic emulsifiers.
 13. The aqueous composition according to claim 1, wherein the aqueous composition contains a mixture of at least two different anionic polyelectrolytes.
 14. The aqueous composition according to claim 13, wherein the at least two different anionic polyelectrolytes are selected from the group consisting of pectins and gellan gum.
 15. The aqueous composition according to claim 1, wherein the aqueous composition contains a mixture of two pectins.
 16. The aqueous composition according to claim 1, wherein the at least one anionic polysaccharide is selected from the group consisting of anionic polysaccharides with at least one of a degree of esterification and a degree of amidation of a carboxy function in the range of 1% to 75% based on a total number of alcohols and carboxy groups.
 17. The aqueous composition according to claim 1, wherein at least one cation selected from the group consisting of Al, Cu, Fe, Mg and Zn are added to the aqueous composition.
 18. The aqueous composition according to claim 1, wherein the aqueous composition contains a crosslinking agent selected from the group consisting of silanes, siloxanes, phenolic resin types, and amines in an amount of 0.01 g/L to 50 g/L.
 19. The aqueous composition according to claim 1, wherein the aqueous composition contains at least one of complex titanium fluorides and zirconium fluorides in an amount of 0.001 g/L to 75 g/L. 